| Judul Artikel | PENURUNAN KADAR LOGAM TIMBAL SECARA BIOSORPSI MENGGUNAKAN Aspergillus niger FNCC 6018 |
| Abstrak | Penelitian mengenai biosorpsi untuk menurunkan kadar logam Pb telah dilakukan dengan menggunakan biomassa Aspergillus niger FNCC 6018. Penelitian ini bertujuan untuk mengetahui kondisi optimum biosorpsi logam timbal oleh biomassa A. niger FNCC 6018 dengan beberapa variabel meliputi pH, waktu kontak, dan ukuran biosorben. Biomassa kering dari A. niger FNCC 6018 disebut biosorben diperoleh dengan menumbuhkan isolat A. niger FNCC 6018 pada media YEPD (Yeast Extract Peptone Dextrose) dan diinkubasi selama 14 hari pada suhu ruang. Biomassa yang telah tumbuh selanjutnya dimatikan dalam penangas selama 20 menit pada suhu 100ºC dan dicuci dengan akuabides sampai 3 kali kemudian dikeringkan dalam oven selama 16 jam pada suhu 60ºC. Biomassa yang telah kering selanjutnya ditumbuk dengan mortar. Variasi pH dilakukan pada rentang pH 2 sampai 5 dan waktu kontak 0, 10, 20, 30, 45, 60, 75, 90, dan 120 menit. Variasi ukuran biosorben yang dipakai adalah 44, 60, dan 80 mesh. Kadar logam Pb yang terserap diukur dengan menggunakan AAS (Atomic Absorption Spectrometer). Hasil penelitian menunjukkan bahwa pH, waktu kontak, dan ukuran biosorben berpengaruh pada biosorpsi logam Pb oleh biosorben. Kondisi optimum biosorpsi logam Pb oleh A. niger FNCC 6018 terjadi pada rentang pH 2 sampai 3, waktu kontak 30 menit, dan ukuran biosorben 80 mesh. Persentase penurunan kadar logam Pb pada kondisi optimum sebesar 83,68%. |
| Abstrak (Inggris) | The research about biosorption to reduce levels of Pb metal has been carried out using biomass of Aspergillus niger FNCC 6018. This research was aimed to determine the optimum condition of biosorption lead metal by A. niger FNCC 6018 biomass with some of variables include pH, interaction time, and size of biosorben. Dried biomass of A. niger FNCC 6018 as biosorbent was obtained by growing A. niger FNCC 6018 isolate in YEPD (Yeast Extract Peptone Dextrose) medium for 14 days of incubation time at room temperature. Biomass that already grown was killed by heating it at 100ºC temperature for 20 minutes and washed by akuabides for 3 times then drying it at 60ºC temperature for 16 hours. Dried biomass was pounded by a mortar.Various pH treatment conducted at pH range 2 to 5, and interaction time were 0, 10, 20, 30, 45, 60, 75, 90, and 120 minutes. Various of biosorben size were 44, 60, and 80 mesh. Measurement of levels of lead metal adsorbed in each variable was determined by AAS (Atomic Absorption Spectrometer). The results showed that pH, interaction time, and the size of biosorben were influences on lead metal biosorption by biosorben. Optimum condition biosorption of lead metal by A. niger FNCC 6018 were occurred at pH 2 to 3, the interaction time were 30 minutes, and the size of biosorben was 80 mesh. The percentage decrease of lead metal content at the optimum condition was 83.68%. |
| Kata Kunci | biosorpsi, logam Pb, Aspergillus niger FNCC 6018, AAS |
| Nama Pembimbing 1 | Zusfahair, S.Si., M.Si |
| Nama Pembimbing 2 | Tien Setyaningtyas, S.Si., M.Si |
| Tahun | 2012 |
| Jumlah Halaman | 64 |
Page generated in 0.0519 seconds.