| Judul Artikel | ADSORPSI LOGAM KADMIUM (Cd) OLEH BIOMASSA SERBUK KULIT SINGKONG (Manihot utilissima) PADA pH DAN WAKTU KONTAK YANG BERBEDA |
| Abstrak | Kajian adsorpsi logam kadmium (Cd) oleh biomassa kulit singkong (Manihot utilissima) pada berbagai pH dan waktu kontak telah dilakukan. Penelitian dilakukan dengan tujuan untuk mengetahui adsorpsi optimum logam kadmium oleh kulit singkong berdasarkan pH (level 3, 4, 5, 6) dan waktu kontak (level 20, 50, 80, 110 menit) serta untuk mengetahui apakah sisa hasil adsorpsi logam kadmium oleh kulit singkong berada di bawah ambang baku mutu kadmium bagi lingkungan. Penelitian dilakukan secara eksperimental dengan RAL pola faktorial (pH dan waktu kontak) kemudian dianalisis menggunakan uji F dilanjut dengan BNJ. Hasil penelitian belum menunjukkan optimum adsorpsi, namun adsorpsi terbaik terdapat pada pH 3 dengan waktu kontak 110 menit sebesar 73,18 mg/L atau 36,59 % (P<0,05). Hasil tersebut diduga karena pada pH 3 kelarutan logam tinggi dan interaksi elektrostatis yang kuat antara logam kadmium dengan situs aktif pada permukaan kulit singkong. Selanjutnya pada waktu kontak 110 menit diduga karena besarnya waktu kontak dengan ketersediaan yang tinggi dari situs aktif pada permukaan kulit singkong. Kesimpulan penelitian ini adalah kapasitas maksimum adsorpsi logam kadmium oleh Manihot utilissima sebesar 73,18 mg/L dengan adsorpsi terbaik pada pH 3 dengan waktu kontak 110 menit dan sisa hasil adsorpsi masih berada di atas ambang baku mutu kadmium bagi lingkungan. |
| Abstrak (Inggris) | A study of adsorption cadmium metal (Cd) by cassava peel (Manihot utilissima) biomass at various pH and contact time was conducted. The study was to know adsorption optimum of cadmium metal by cassava peel based on pH (3, 4, 5 and 6) and contact time (20, 50, 80 and 110 minute); to know whether adsorption cadmium residue by cassava peels would be compared with threshold standart environment. Experimental method with CRD in factorial pattern was used and then data were F-tested and followed with HSD. The results showed that the best adsorption at pH 3 with a contact time of 110 minutes was 73.18 mg/L or 36.59% (P<0.05). The results at pH 3 because high metal solubility and strong electrostatic interactions between the metal cadmium with active sites on cassava peel surface. Furthermore, 110 minutes contact time caused the amount of contact time and high availability of active sites on the surface of the skin cassava. Conclusion that maximum adsorption capacity of the metal cadmium by Manihot utilissima reached to 73.18 mg/L. The best adsorption at pH 3 with a contact time of 110 minutes. The rest of the adsorption results were still above the threshold standards for environmental cadmium. |
| Kata Kunci | Kata kunci : Kulit singkong, adsorpsi, logam kadmium, pH, waktu kontak. |
| Nama Pembimbing 1 | Nuning Vita Hidayati, S.Pi, M.Si |
| Nama Pembimbing 2 | Drs. Asrul Sahri Siregar, M.Si |
| Tahun | 2014 |
| Jumlah Halaman | 10 |
Page generated in 0.0548 seconds.