Judul ArtikelSINTESIS DAN UJI EFEKTIVITAS FOTOKATALIS POLIANILIN/TiO2 TERHADAP DEGRADASI SENYAWA RHODAMIN B
AbstrakDegradasi zat warna rhodamin B telah dilakukan dengan menggunakan fotokatalis Polianilin/TiO2 yang disintesis menggunakan metode polimerisasi. Garam emeraldine dari Polianilin dan Polianilin/TiO2 yang dihasilkan berwarna hijau. Fotokatalis dikarakterisasi menggunakan SEM (Scanning Electron Microscopy), EDX(Energy Dispersive XRay Spectroscopy), dan FTIR (Fourier TransformInfra-Red). Penambahan 1%, 5% dan 10% (b/b) TiO2 diketahui dapat meningkatkan aktivitas fotokatalitik polianilin. Fotokatalis Polianilin/TiO2 1% terbukti memberikan penurunan degradasi rodamin b tertinggi yaitu sebesar 53%. Degradasi rhodamin meningkat sebesar 80% pada suasana basa yaitu pada pH 9 dengan waktu optimum 300 menit dibawah sinar tampak lampu tungsten. Laju kinetika diperoleh mengikuti orde satu dengan konstanta laju fotodegradasi rhodamin B 20 ppm sebesar 0,005445 menit-1. uji penggunaan kembali(reusable) dilakukan sebanyak 5 kali dengan menghasilkan persen degradasi terakhir sebesar 27%, hal ini dapat dikatakan bahwa Polianilin/TiO2 memiliki sifat kurang stabil jika digunakan berulang kali yang dapat disebabkan oleh berkurangnya konduktivitas polianilin.
Abstrak (Inggris)The degradation of rhodamine b dye was carried out using a Polyaniline / TiO2 photocatalyst which was synthesized using the polymerization method. The emeraldine salts of Polyaniline and Polyaniline/TiO2 shows in green color. Photocatalysts were characterized using SEM (Scanning Electron Microscopy), EDX (Energy Dispersive XRay Spectroscopy), and FTIR (Fourier Transform Infra-Red). The addition of 1%, 5% and 10% (w/w) TiO2 was found to increase the photocatalytic activity of polyaniline. photocatalyst Polyaniline/TiO2 1% was proven to provide the highest reduction in rhodamine b degradation, 53%. Rhodamine degradation increased by 80% in alkaline conditions, at pH 9 with an optimum time of 300 minutes under visible light from a tungsten lamp. The rate of kinetics was obtained following order one with a constant rate of photodegradation of rhodamine b 20 ppm of 0.005445 minutes-1. reusable test was carried out 5 times with the last percentage degradation of 27%, it can be said that Polyaniline / TiO2 has less stable properties if used repeatedly which can be caused by the reduced conductivity of polyaniline.
Kata KunciPolianilin/TiO2, Rhodamin B, aktivitas fotokatalitik, reusable
Nama Pembimbing 1Roy Andreas, S.Si., M.Si., Ph.D
Nama Pembimbing 2Irmanto, S.Si., M.Si
Tahun2020
Jumlah Halaman37
Page generated in 0.0507 seconds.