| Judul Artikel | PEMBUATAN MATERIAL PIEZOELEKTRIK BISMUTH NATRIUM TITANATE-STRONTIUM TITANATE (BNT-ST) DOPING Mn2O3 DENGAN METODE SOLID STATE REACTION DAN KARAKTERISASINYA |
| Abstrak | Piezoelektrik merupakan fenomena listrik yang dihasilkan dari material padat dan kristal ketika material itu ditekan atau dikenai gaya eksternal. Material piezoelektrik yang paling banyak digunakan adalah Lead Zirconate Titanate (PZT) dengan kandungan 60% Timbal (Pb) dari komposisinya dan memiliki potensi berbahaya bagi lingkungan. Pada penelitian ini telah dilakukan pembuatan dan karakterisasi material piezoelektrik bebas timbal yang ramah lingkungan yaitu Bismuth Natrium Titanate-Strontium Titanate (BNT-ST) doping Mn2O3 menggunakan metode Solid State Reaction. Variasi konsentrasi doping Mn2O3 adalah 1, 2, 3, dan 4 dalam %mol. Pengujian karakterisasi dilakukan menggunakan X-Ray Diffraction (XRD), SEM-EDS, dan Electrochemical Impedance Spectroscopy (EIS). Material Bismuth Natrium Titanate-Strontium Titanate (BNT-ST) doping Mn2O3 menghasilkan tiga fasa kristal berupa Bi0,7Sr0,3MnO3, Bi4,5Na0,5Ti4O15, dan Na2Ti9O19 dengan struktur kristal berturut-turut yaitu orthorhombik, tetragonal, dan monoklinik. Komposisi optimumnya yaitu pada pemberian konsentrasi doping 4%mol Mn2O3 yang memiliki pola difraksi dengan puncak tertinggi di 2θ = 32,54°, nilai impedansi sebesar Z = 0,21 Ω, dan konstanta dielektrik sebesar εr = 1197 pada frekuensi tinggi 0,25 MHz dengan temperatur pengujian sampel sebesar T = 275°C. |
| Abstrak (Inggris) | Piezoelectric is an electrical phenomenon that is produced from solid and crystalline materials when the material is pressed or subjected to an external force. The most widely used piezoelectric material is Lead Zirconate Titanate (PZT) which contains 60% Lead (Pb) of its composition and potentially damaging for environment. In this research has carried out the fabrication and characterization of environmentally friendly lead-free piezoelectric material, namely Bismuth Natrium Titanate-Strontium Titanate (BNT-ST) doping Mn2O3 using the solid state reaction method. The variation of Mn2O3 doping concentration is 1, 2, 3, and 4 in %mol. Characterization tests were performed using X-Ray Diffraction (XRD), SEM-EDS, and Electrochemical Impedance Spectroscopy (EIS). Material Bismuth Natrium Titanate-Strontium Titanate (BNT-ST) doping Mn2O3 produces three crystal phases in the form of Bi0,7Sr0,3MnO3; Bi4,5Na0,5Ti4O15; and Na2Ti9O19 with consecutive crystal structures in the form of orthorhombik, tetragonal, and monoclinic. The optimum composition is the doping concentration of 4%mol Mn2O3 which has a diffraction pattern with the highest peak intensity at 2θ = 32.54°, an impedance value of Z = 0.21 Ω, and a dielectric constant of εr = 1197 at a high frequency of 0.25 MHz with a sample experimental temperature of T = 275°C. |
| Kata Kunci | Bismuth Natrium Titanate-Strontium Titanate (BNT-ST) doping Mn2O3, Bebas timbal, Solid State Reaction, Impedansi, Dielektrik. |
| Nama Pembimbing 1 | Dr. Eng. Mukhtar Effendi |
| Nama Pembimbing 2 | Sugito, M.Si |
| Tahun | 2021 |
| Jumlah Halaman | 14 |
Page generated in 0.0651 seconds.